CC=92531 Help
TitleThe crystal chemistry of superconducting Sr3.66 Bi0.28 Ca6.02 Cu16.45 O28.63 and nonsuperconducting Sr5.97 Ca3.13 Y0.53 Al0.25 Bi0.12 Cu16.66 O28.64 compounds.
AuthorsShvanskaya, L.;Leonyuk, L.;Sokolova, E.;Maltsev, V.
ReferenceZeitschrift fuer Kristallographie (2000) 215, 368-372
Link XRef SCOPUS Google
CompoundAl0.26 Bi0.12 Ca3.128 Cu16.537 O28.476 Sr5.964 Y0.534 - Bismuth aluminium yttrium calcium strontium copper oxide (0.12/0.26/0.53/3.13/5.96/16.54/28.48) [A20B33X57] [oF220] [k9 j h3 g2 f e2 d b] []
Cell11.346(3), 12.996(3), 19.5850(90), 90., 90., 90.
F222 (22) V=2887.86
RemarksR=0.077000 : D
At least one temperature factor is implausible or meaningless but agrees with the value given in the paper.

Atom (site) Oxid. x, y, z, B, Occupancy
Ca1(16k)2
Sr1(16k)2
Bi1(16k)3
Al1(16k)3
Ca2(8f)2
Sr2(8f)2
Bi2(8f)3
Y1(8f)3
Al2(8f)3
Ca3(16k)2
Sr3(16k)2
Bi3(16k)3
Al3(16k)3
Cu1(8e)2.178
Cu2(16k)2.178
Cu3(16k)2.178
Cu4(8h)2.178
Cu5(8h)2.178
Cu6(4d)2.178
Cu7(8h)2.178
O1(8g)-2
O2(8g)-2
O3(4b)-2
O4(8e)-2
O5(16k)-2
O6(16k)-2
O7(8j)-2
O8(16k)-2
O9(16k)-2
O10(16k)-2
-.000.120.8000.32
-.000.120.8000.63
-.000.120.8000.01
-.000.120.8000.02
00.370.500.27
00.370.500.39
00.370.500.02
00.370.500.26
00.370.500.03
-.000.860.6000.32
-.000.860.6000.65
-.000.860.6000.00
-.000.860.6000.02
0.1600.500.97
0.160.000.1000.98
0.16-.000.2900.96
0.250.250.1700.96
0.250.250.0300.98
0.250.250.7500.91
0.250.250.8900.97
000.3000.99
000.1001
000.50.000.99
0.160000.97
0.17-.000.1901
0.16-.000.5900.99
0.130.250.2500.99
0.130.220.1000.95
0.140.230.5300.99
0.130.230.6700.94
Atom (site) Oxid. U11, U22, U33, U12, U13, U23
Ca1(16k)2
Sr1(16k)2
Bi1(16k)3
Al1(16k)3
Ca2(8f)2
Sr2(8f)2
Bi2(8f)3
Y1(8f)3
Al2(8f)3
Ca3(16k)2
Sr3(16k)2
Bi3(16k)3
Al3(16k)3
Cu1(8e)2.178
Cu2(16k)2.178
Cu3(16k)2.178
Cu4(8h)2.178
Cu5(8h)2.178
Cu6(4d)2.178
Cu7(8h)2.178
O1(8g)-2
O2(8g)-2
O3(4b)-2
O4(8e)-2
O5(16k)-2
O6(16k)-2
O7(8j)-2
O8(16k)-2
O9(16k)-2
O10(16k)-2
0.000.010.01-.000.00-.00
0.000.010.01-.000.00-.00
0.000.010.01-.000.00-.00
0.000.010.01-.000.00-.00
0.010.000.010-.000
0.010.000.010-.000
0.010.000.010-.000
0.010.000.010-.000
0.010.000.010-.000
0.000.000.01-.00-.00-.00
0.000.000.01-.00-.00-.00
0.000.000.01-.00-.00-.00
0.000.000.01-.00-.00-.00
0.000.020.00000.00
0.000.020.00-.00-.000.00
0.000.010.000.00-.000.00
0.000.010.060.0000
0.000.020.050.0000
0.000.010.04000
0.000.010.07-.0000
0.000.060.000.0000
0.000.020.010.0000
000000
0.000.030.00000.00
0.000.010.000.00-.000.00
0.000.010.000.000.00-.00
0.020.060.0500-.03
0.000.020.050.00-.010.01
0.000.020.06-.000.000.01
0.000.040.060.000.00-.02

Demo database


Copying or publishing either the ICSD data or software without written permission is illegal.
The ICSD database is copyright © 2018 by Fachinformationszentrum (FIZ) Karlsruhe
The PHP-mySQL WWW interface is copyright © 2003-2015 by Peter Hewat
The 3D crystal structure visualisation software, xtal-3d is copyright © 1994-2015 by Marcus Hewat
The PHP-JMOL drawing software is copyright © 2006-2015 by Alan Hewat
Please report technical problems with ICSD for WWW to alan.hewat[a]neutronoptics.com (Alan Hewat).